valve FEP pellets 605 for linning with good quality

FOB Reference Price:Get Latest Price
US $3-6 / Kilogram | 500 Kilogram/Kilograms (Min. Order)
Supply Ability:
300 Ton/Tons per Month
Port:
qingdao,china
Report Suspicious Activity
Overview
Quick Details
CAS No.:
25067-11-2
Other Names:
fep
MF:
-[(CF2-CF2)x-(CF2-CF)y]n-
EINECS No.:
None
Place of Origin:
Shandong, China (Mainland)
Type:
Synthetic Resin and Plastics
Brand Name:
PURVAN
Model Number:
601
Purity:
100%
apperance:
white powder
test:
SGS CIQ BV
sample:
free
certificate:
REACH ISO CE
Packaging & Delivery
Packaging Details
Packaging Detail: 1.Hot sale 100% purity FEP powder 605/606 price 2.The resin is packed in double layer PVC bags , then closed in hard drums outside, 25kg per drum with certification.
Delivery Detail: 1 week after deposit received
Delivery Time
Shipped in 3 days after payment

Specifications

1.Hot sale 100% purity FEP powder 605/606 price 
2.FEP powder used for wire insulation layer 
3FEP powder with SGS

Specifications

Unsintered thread sealing tape 
thin-walled tubes 
cable insulating layers

PTFE Fine Powder 203A Extrusion grade

Unsintered thread sealing tape
thin-walled tubes
cable insulating layers

 

Specification:

 

Properties

Test method

Test condition

Unit

FR203A-1

FR203A-2

 

Physical

properties

Standard specifi

gravity

GB/T 1033.1

Method A

Testing Temperature:23°C

/

2.14~2.17

2.16~2.20

Thermal instability

index

GB/T1033.1HG/T2902

Method A

Testing Temperature:23°C

/

≤50

Bulk density

HG/T2900

Testing Temperature:23°C±5°C

g/L

500±100

Average partical

size

HG/T2901

Dry screening

µm

500±150

Moisture content

Infrared moisture

analyzer

/

%

≤0.02

Thermal

properties

Melting peak

temperature

HG/T2902

Second melting peak

temperature

°C

372±5

Mechanical

properties

Tensile strength

GB/T1040.1

HG/T2902

Tensile Speed:100mm/min

Mpa

≥32.0

≥28.0

Elongation at break

GB/T1040.1

HG/T2902

Tensile Speed:100mm/min

%

≥400

≥300

Extrusion pressure

HG/T2899

a,Reduction ratio:400:1

b,Reduction ratio:100:1

Mpa

10±20a

10±5b